Fluorocarbon coating
Fluorocarbon Aluminum composite panel is made with fluorine enyne as the basic monomer, mixed with fluorocarbon resin, paint, alcohol ester solvent and accessory ingredients. The molecular structure in the coating becomes compact after being high baked to create a filmwhich has extra strong weather resistance../to create an extra weather resistant film.
The fluorocarbon coating falls into conventional fluorocarbon coating or nano fluorocarbon coating according to the structure of film formation on the surface.
A.Conventional fluorocarbon is made of KYNAR500 fluorocarbon and is solidified to create the film on the surface after three coats and three bakes. It is acid and alkali resistant, standing the test of severe environment, and has no abnormal depigmentation for 15 to 20 years. It is more suitable for exterior decoration of architectures and curtain wall decoration of major constructional projects that have high demand for weather resistance.
B.Nano fluorocarbon is made of matured fluorocarbon surface processed with an additional coating of stain resistant layer added with nano materials. The coating after film formation has an extra low surface tension, which is stain resistant and can clean its surface coating simply by natural rain washing.
| Raw Material | Product Specifications | ||||||||
|
|
Product Data Sheet
Pivot ACM( architecture )
| Panel Thickness | Standard | Unit | 3mm | 4mm | 6mm |
| Thickness of Aluminium | DIN 1784 | mm | 0.5 | 0.5 | 0.5 |
| Aluminum thickness deviation | DIN 1784 | mm | ±0.01 | ±0.01 | ±0.01 |
| Weight | Kg/m2 | 4.65 | 5.63 | 7.42 | |
| Tolerance in length | DIN 16927 / ISO 11833-1 | mm | - 1 / +3 | - 1/ +3 | - 1/ +3 |
| Tolerance in width | DIN 16927 / ISO 11833-1 | mm | - 1 / +1.5 | - 1 / +1.5 | - 1 / +1.5 |
| Tolerance in thickness | DIN 16927 / ISO 11833-1 | mm | ± 0.15 | ± 0.15 | ± 0.15 |
| Horizontal flatness | DIN ISO 1101 | mm | 6 | 5 | 5 |
| Longitudinal roughness | DIN ISO 1101 | mm | 7 | 6 | 6 |
| Technical Properties | |||||
| Section Modulus W | DIN 53293 | cm3/m | 1.25 | 1.75 | 2.75 |
| Rigidity (Poisson's ratio μ = 0.3) E.J | DIN 53293 | kNm2/m | 0.14 | 0.28 | 0.63 |
| Alloy | EN 573-3 | ENAW | 1100 | ||
| Temper of Cover Sheets | EN 515 | H16/H18 | |||
| Modulus of Elasticity | EN 1999 1-1 | N/mm2 | 70,000 | ||
| Tensile Strength of Aluminium | EN 485-2 | N/mm2 | Rm ≥ 145 | ||
| 0.2% Proof Stress | EN 485-2 | N/mm2 | Rp0.2 ≥ 100 | ||
| Elongation | EN 485-2 | % | A50 ≥ 2 | ||
| Linear Thermal Expansion | EN 1999 1-1 | mm/m/℃ | 2.4 at 100℃ Temp difference | ||
| Core | |||||
| Polyethylene, Typ LD-PE | g/cm3 | 0.935 | |||
| Surface | Coil Coating | ||||
| Lacquering | Fluorocarbon based (PVdF) | ||||
| Thickness of coating | µm | two coating：≥26，three coating:≥32 | |||
| Gloss (initial value) | ECCA T2 | % | 30 - 80 | ||
| Pencil Hardness | ECCA T4 | H | |||
| Acoustical Properties | |||||
| Sound Absorption Factor άs | ISO 354 | 0.05 | |||
| Sound Transmission Loss RW | ISO 717-1 | DB | 25 | 26 | 28 |
| Loss Factor d | EN ISO 6721 | 0.0072 | 0.0087 | 0.0138 | |
| Thermal Properties | |||||
| Thermal Resistance R | DIN 52612 | m2K/W | 0.0069 | 0.0103 | 0.0172 |
| Heat Transition Coefficient U | DIN 4108 | W/m2K | 5.65 | 5.54 | 5.34 |
| Temperature Range | ℃ | -50…+80 | |||
| fire-protection rating | EN—13501 | ||||